Electrodes et fils fourrés





STEELOR Electrodes Of Recharging




STEELARC 2963
Data Sheet
Rutile electrode -all positions - for recharging of machine elements or underlayer of hard rechargings - Very high impact resistance and to cracking - Usinable.
Hardness: 250 HB
STEELARC 5963
Data Sheet
Rutile electrode - all positions - Facility of employment for rechargings subjected to an average abrasion and average shocks - easily detachable Slag.
Hardness: 580-600 HB
STEELARC 6935
Data Sheet
Electrode for rechargings subjected to a severe abrasion and shocks very violent one - Parts of breakers - Teeth of cups - Weak slag.
Hardness: 59-61 HRC
STEELARC 6324
Data Sheet
Electrode depositing an alloy in content raised with manganese - the deposit carried out is hammer-hardenable with the shocks and is appropriate well for the recharging of parts for manganese subjected to shocks violent one and an important abrasion - also Used as underlayer before hard rechargings. Employment: rechargings of parts of breakers and crushers, hammers of percussion, beaters, jaws and all the components subjected to the pressures, shocks and crushings.
Hardness: 200 to 250 HB hammer-hardening to 400/500 HB
STEELARC 6345


Data Sheet
Electrode depositing an alloy in content raised with manganese and chromium - the deposit carried out is hammer-hardenable with the shocks and is appropriate well for the recharging of parts for manganese subjected to shocks violent one and a severe abrasion - also Used for the assembly of manganese steels and the repair of the components of ways of railroad - Underlayer before hard rechargings on manganese steels and pig iron and cast iron with chromium. Employment: rechargings of parts of crushers and breakers, hearts of ways of railroad, underlayers and connections interlayers for hard recharging.
Hardness: 220 HB  hammer-hardening to 55 HRC
STEELARC 9356
Data Sheet
Electrode depositing an alloy of the cast iron type to chromium particularly resistant to abrasion under weak shocks with means - Used in all the cases of wear by the ground, sand, the abrasives. Employment: pumps of dredging, mixers, sheets of screens, screws conveying, arm of mixers.
Hardness: 62-63 HRC
STEELARC 1A
Data Sheet
Tubular special electrode depositing a chromium carbide alloy strongly charged. Extremely resistant to abrasion under effect of average shocks to weak - Small hammer-hardenable effect with work. Employment: blades of cups, screen and armour plates, parts of crushers, arm of mixers, hammers of garbage disintegrators, etc.
Hardness: stamp = 560 to 600 HV - Carbide: 1.000 to 1.100 HV
STEELARC 9563
Data Sheet
Electrode depositing an alloy strongly charged out of chromium carbides and nobium extremely resistant to abrasion. Advised in the cases of very important wears under average shocks. Employment: screw of transport, screw of moulding machines , teeth of dragline excavator, A.F.C. chains, scrapers various, blast furnace cones, screens, stirring arm, pump wheels.
Hardness: 63-66 HRC
STEELARC 9365

Data Sheet
Electrode depositing complex a carbide alloy strongly charged, extremely resistant to abrasion, with oxidation and with erosion until 650 °C. Employment:  blast furnace cones; agglomeration of iron and steel industry, screens heat, heads of screw moulding machines, parts of crushers working under weak shocks and strong pressures, parts with manganese, clod-crusher, etc
Hardness: 64-66 HRC 20 °C - 40-45 HRC 600 °C
STEELARC 9666

Data Sheet
Electrode depositing a carbide alloy strongly charged with chromium and complex carbides - recharging obtained has a particularly high hardness and its resistance to abrasion is very extreme - Usable in position. Employment: mixer or stirring arm, screw of extrusion, fanblades, propellers, parts of wears and cement factory, iron and steel industry, brickyards.
Hardness: 68-70 HRC
STEELARC 9777

Data Sheet
High capacity electrode depositing a carbide alloy charged with chromium and vanadium, particularly resistant to wear by severe abrasion, combined with moderate shocks and high temperatures. Employee for the recharging of screw, fanblades and head the moulding machines, blades and arm of mixers, crushers of glass and abrasive ores, trailing chains, buckets of dragline excavator and machines for special foundations, screw of drilling.
Hardness: 65 - 67 HRC.